Aluminium has a low density- 2700 kg / m3 (2.7 g / cm3), low melting point (660 ° C), high ductility, and thermal conductivity. It is easy to rolling, forging, drawing, and other processing. The form in this case of semi-finished products and aluminum used relatively infrequently, because it has low strength [50-80 MN / m2 (8.5 kgf / mm)] and a hardness (HB 20-30), but at the same time it alloys with other elements have a whole list of useful mechanical and physical properties, which are widely used in almost all aviation sectors and mechanical engineering.

In order to provide maximum opportunities selecting suitable alloys to our customers, depending on the equipment used by them and the final product destination (for consumers in Russia / CIS or UES, etc..), «Orion-Spetсsplav-Gatchina» Ltd. is able to offer a variety of alloys, produced as a GOST (4784-74 or 1583-93), and like DIN EN 1706 or other international standards (see below):

Casting and wrought aluminum alloys according to DIN EN1706

 
  other elements
Designation based on chemical symbols EN AC- : Digital designation EN AC- : Al Si Fe Cu Mn Mg Cr Ni Zn Pb Sn Ti each total
Al Cu4 Mg Ti 21000 basis 0,20 (0,15) 0,35 (0,30) 4,2-5,0 0.10 0,15-0,35 (0,20-0,35)   0.05 0.10 0.05 0.05 0,15-0,30 (0,15-0,25) 0.03 0.10
Al Cu4 Ti 21100 basis 0,18 (0,15) 0,19 (0,15) 4,2-5,2 0.55       0.07     0,15-0,30 (0,15-0,25) 0.03 0.10
Al Si2 Mg Ti 41000 basis 1,6-2,4 0,60 (0,50) 0,10 (0,08) 0,30-0,50 0,45-0,65 (0,50-0,65)   0.05 0.10 0.05 0.05 0,05-0,20 (0,07-0,15) 0.05 0.15
Al Si7 Mg 42000 basis 6,5-7,5 0,55 (0,45) 0,20 (0,15) 0.35 0,20-0,65 (0,25-0,65)   0.15 0.15 0.15 0.05 0,05-0,25 (0,05-0,20) 0.05 0.15
Al Si7 Mg0,3 42100 basis 6,5-7,5 0,19 (0,15) 0,05 (0,03) 0.10 0,25-0,45 (0,30-0,45)     0.07     0,08-0,25 (0,10-0,18) 0.03 0.10
Al Si7 Mg0,6 42200 basis 6,5-7,5 0,19 (0,15) 0,05 (0,03) 0.10 0,45-0,70 (0,50-0,70)     0.07     0,08-0,25 (0,10-0,18) 0.03 0.10
Al Si10 Mg (A) 43000 basis 9,0-11,0 0,55 (0,40) 0,05 (0,03) 0.45 0,25-0,45 (0,30-0,45)   0.05 0.10 0.05 0.05 0.15 0.05 0.15
Al Si10 Mg (B) 43100 basis 9,0-11,0 0,55 (0,40) 0,10 (0,08) 0.45 0,20-0,45 (0,25-0,45)   0.05 0.10 0.05 0.05 0.15 0.05 0.15
Al Si10 Mg (Cu) 43200 basis 9,0-11,0 0,65 (0,55) 0,35 (0,30) 0.55 0,20-0,45 (0,25-0,45)   0.15 0.35 0.05 0.05 0.15 0.05 0.15
Al Si9 Mg 43300 basis 9,0-10,0 0,19 (0,15) 0,05 (0,03) 0.10 0,25-0,45 (0,30-0,45)     0.07     0.15 0.03 0.10
Al Si10 Mg (Fe) 43400 basis 9,0-11,0 1,0 (0,45-0,90) 0,10 (0,08) 0.55 0,20-0,50 (0,25-0,50)   0.15 0.15 0.15 0.05 0,20 (0,15) 0.05 0.15
Al Si11 44000 basis 10,0-11,8 0,19 (0,15) 0,05 (0,03) 0.10 0.45     0.07     0.15 0.03 0.10
Al Si12 (B) 44100 basis 10,5-13,5 0,65 (0,55) 0,15 (0,10) 0.55 0.10   0.10 0.15 0.10   0,20 (0,15) 0.05 0.15
Al Si12 (A) 44200 basis 10,5-13,5 0,55 (0,40) 0,05 (0,03) 0.35       0.10     0.15 0.05 0.15
Al Si12 (Fe) 44300 basis 10,5-13,5 1,0 (0,45-0,90) 0,10 (0,08) 0.55       0.15     0.15 0.05 0.25
Al Si9 44400 basis 8,0-11,0 0,65 (0,55) 0,10 (0,08) 0.50 0.10   0.05 0.15 0.05 0.05 0.15 0.05 0.15
Al Si6 Cu4 45000 basis 5,0-7,0 1,00 (0,90) 3,0-5,0 0,20-0,65 0.55 0.15 0.45 2.00 0.30 0.15 0,25 (0,20) 0.05 0.35
Al Si5 Cu3 Mg 45100 basis 4,5-6,0 0,60 (0,50) 2,6-3,6 0.55 0,15-0,45 (0,20-0,45)   0.10 0.20 0.10 0.05 0,25 (0,20) 0.05 0.15
Al Si5 Cu3 Mn 45200 basis 4,5-6,0 0,80 (0,70) 2,5-4,0 0,20-0,55 0.40   0.30 0.55 0.20 0.10 0,20 (0,15) 0.05 0.25
Al Si5 Cu1 Mg 45300 basis 4,5-5,5 0,65 (0,55) 1,0-1,5 0.55 0,40-0,65 (0,35-0,65)   0.25 0.15 0.15 0.05 0,05-0,20 (0,05-0,25) 0.05 0.15
Al Si5 Cu3 45400 basis 4,5-6,0 0,60 (0,50) 2,6-3,6 0.55 0.05   0.10 0.20 0.10 0.05 0,25 (0,20) 0.05 0.15
Al Si9 Cu3 (Fe) 46000 basis 8,0-11,0 1,30 (0,60-1,10) 2,0-4,0 0.55 0,05-0,55 (0,15-0,55) 0.15 0.55 jaan.20 0.35 0.25 0,25 (0,20) 0.05 0.25
Al Si11 Cu2 (Fe) 46100 basis 10,0-12,0 1,10 (0,45-1,0) 1,5-2,5 0.55 0.30 0.15 0.45 jaan.70 0.25 0.25 0,25 (0,20) 0.05 0.25
Al Si8 Cu3 46200 basis 7,5-9,5 0,80 (0,70) 2,0-3,5 0,15-0,65 0,05-0,55 (0,15-0,55)   0.35 jaan.20 0.25 0.15 0,25 (0,20) 0.05 0.25
Al Si7 Cu3 Mg 46300 basis 6,5-8,0 0,80 (0,70) 3,0-4,0 0,20-0,65 0,30-0,60 (0,35-0,60)   0.30 0.65 0.15 0.10 0,25 (0,20) 0.05 0.25
Al Si9 Cu1 Mg 46400 basis 8,3-9,7 0,80 (0,70) 0,8-1,3 0,15-0,55 0,25-0,65 (0,30-0,65)   0.20 0.80 0.10 0.10 0,10-0,20 (0,10-0,18) 0.05 0.25
Al Si9 Cu3 (Fe) (Zn) 46500 basis 8,0-11,0 1,30 (0,60-1,20) 2,0-4,0 0.55 0,05-0,55 (0,15-0,55) 0.15 0.55 3.00 0.35 0.25 0,25 (0,20) 0.05 0.25
Al Si7 Cu2 46600 basis 6,0-8,0 0,80 (0,70) 1,5-2,5 0,15-0,65 0.35   0.35 1.00 0.25 0.15 0,25 (0,20) 0.05 0.15
Al Si12 (Cu) 47000 basis 10,5-13,5 0,80 (0,70) 1,00 (0,90) 0,05-0,55 0.35 0.10 0.30 0.55 0.20 0.10 0,20 (0,15) 0.05 0.25
Al Si12 Cu1 (Fe) 47100 basis 10,5-13,5 1,30 (0,60-1,10) 0,7-1,2 0.55 0.35 0.10 0.30 0.55 0.20 0.10 0,20 (0,15) 0.05 0.25
Al Si12 Cu Ni Mg 48000 basis 10,5-13,5 0,70 (0,60) 0,8-1,5 0.35 0,8-1,5 (0,9-1,5)   0,7-1,3 0.35     0,25 (0,20) 0.05 0.15
Al Mg3 (B) 51000 basis 0,55 (0,45) 0,55 (0,45) 0,10 (0,08) 0.45 2,5-3,5 (2,7-3,5)     0.10     0,20 (0,15) 0.05 0.15
Al Mg3 (A) 51100 basis 0,55 (0,45) 0,55 (0,40) 0,05 (0,03) 0.45 2,5-3,5 (2,7-3,5)     0.10     0,20 (0,15) 0.05 0.15
Al Mg9 51200 basis veebr.50 1,00 (0,45-0,90) 0,10 (0,08) 0.55 8,0-10,5 (6,5-8,5)   0.10 0.25 0.10 0.10 0,20 (0,15) 0.05 0.15
Al Mg5 51300 basis 0,55 (0,35) 0,55 (0,45) 0,10 (0,05) 0.45 4,5-6,5 (4,8-6,5)     0.10     0,20 (0,15) 0.05 0.15
Al Mg5 (Si) 51400 basis 1,50 (1,30) 0,55 (0,45) 0,05 (0,03) 0.45 4,5-6,5 (4,8-6,5)     0.10     0,20 (0,15) 0.05 0.15
Al Zn5 Mg 71000 basis 0,30 (0,25) 0,80 (0,70 0,15-0,35 0.40 0,4-0,7 (0,45-0,7) 0,15
-0,60
0.05 4,5-6,0 0.05 0.05 0,10-0,25 (0,12-0,20) 0.05 0.15
 
 

Wrought and casting aluminum alloys according to GOST 4784-74 and GOST 1583-93

 
  other elements
GOST 4784-74 ММ basis 0.20 0,2-0,5 1,0-1,4 0.10 0.60 1.0 - 0.10 - - -     0.05 0.20
GOST 4784-74 Амц basis 0.10 0.20 1,0-1,6 0.10 0.70 0.60 - 0.20 - - -     0.05 0.10
GOST 4784-74 АМцС basis 0.10 0.05 1,0-1,4 0.10 0,25-0,45 0,15-0,35 - 0.10 - - -     0.05 0.10
GOST 4784-74 Д12 basis 0.10 0,8-1,3 1,0-1,5 0.10 0.70 0.70 - 0.10 - - -     0.05 0.10
GOST 4784-74 АМг1 basis 0.10 0,7-1,6 0.20 - 0.10 0.10 - - - - -     0.05 0.10
GOST 4784-74 АМг2 basis 0.10 1,8-2,6 0,2-0,6 0.20 0.40 0.40 - 0.10 0.05 - -     0.05 0.10
GOST 4784-74 АМг3С basis 0.10 2,7-3,6 0,0-0,6 0.20 0.50 0.50 - 0.20 0.25 - 0,000- 0,005     0.05 0.15
GOST 4784-74 АМг3 basis 0.10 3,2-3,8 0,3-0,6 0.20 0.50 0,5-0,8 - 0.10 0.05 - -     0.05 0.10
GOST 4784-74 АМг4 basis 0.10 3,8-4,5 0,5-0,8 0.20 0.40 0.40 - 0,02-0,1 0,05-0,25 - 0,0002- 0,005     0.05 0.10
GOST 4784-74 АМг4,5 basis 0.10 4,0-4,9 0,4-1,0 0.20 0.40 0.40 - 0.20 0,05-0,25 - 0,000- 0,005     0.05 0.15
GOST 4784-74 АМг5 basis 0.10 4,8-5,8 0,3-0,8 0.20 0.50 0.50 - 0,02-0,1 - - 0,0002- 0,005     0.05 0.10
GOST 4784-74 АМг6 basis 0.10 5,8-6,8 0,5-0,8 0.20 0.40 0.40 - 0,02-0,1 - - 0,0002- 0,005     0.05 0.10
GOST 4784-74 АД31 basis 0.10 0,4-0,9 0.10 0.20 0.50 0,3-0,7 - 0.15 - - -     0.05 0.10
GOST 4784-74 АД33 basis 0,15-0,4 0,8-1,2 0.15 0.25 0.70 0,4-0,8 - 0.15 0,15-0,35 - -     0.05 0.15
GOST 4784-74 АД35 basis 0.10 0,8-1,4 0,5-0,9 0.20 0.50 0,8-1,2 - 0.15 - - -     0.05 0.10
GOST 4784-74 АВ basis 0,1-0,5 0,45-0,9 0,15-0,35 0.20 0.50 0,5-1,2 - 0.15 0.25 - -     0.05 0.10
GOST 4784-74 Д1 basis 3,8-4,8 0,4-0,8 0,4-0,8 0.30 0.70 0.70 0.10 0.10 - - -     0.05 0.10
GOST 4784-74 Д16 basis 3,8-4,9 1,2-1,8 0,3-0,9 0.30 0.50 0.50 0.10 0.10 - - -     0.05 0.10
GOST 4784-74 В65 basis 3,9-4,5 0,15-0,3 0,3-0,5 0.10 0.20 0.25 - 0.10 - - -     0.05 0.10
GOST 4784-74 Д18 basis 2,2-3,0 0,2-0,5 0.20 0.10 0.50 0.50 - 0.10 - - -     0.05 0.10
GOST 4784-74 АК6 basis 1,8-2,6 0,4-0,8 0,4-0,8 0.30 0.70 0,7-1,2 0.10 0.10 - - -     0.05 0.10
GOST 4784-74 АК8 basis 3,9-4,8 0,4-0,8 0,4-1,0 0.30 0.70 0,6-1,2 0.10 0.10 - - -     0.05 0.10
GOST 4784-74 АК4 basis 1,9-2,5 1,4-1,8 0.20 0.30 0,8-1,3 0,5-1,2 0,8-1,3 0.10 - - -     0.05 0.10
GOST 4784-74 АК4-1 basis 1,9-2,7 1,2-1,8 0.20 0.30 0,8-1,4 0.35 0,8-1,4 0,02-0,1 0.10 - -     0.05 0.10
GOST 4784-74 В95 basis 1,4-2,0 1,8-2,8 0,2-0,6 5,0-7,0 0.50 0.50 0.10 0.05 0,1-0,25 - -     0.05 0.10
GOST 4784-74 Ацпл basis - - 0.03 0,9-1,3 0.30 0.30 - 0.15 - - -     0.05 0.10
GOST 1583-93 АК12 basis 0.60 0.10 0.50 0.30 0.70 10,0-13,0 - 0.10 - 0.1 - - - 0.02 2.1
GOST 1583-93 АК12пч basis 0.02 Ca 0,08 0.08 0.06 0.35 10,0-13,0 - 0.08 - - - - - 0.02 -
GOST 1583-93 АК12оч basis 0.02 Ca 0,04 0.03 0.04 0.20 10,0-13,0 - 0.03 - - - - - 0.02 -
GOST 1583-93 АК12М2 basis 1,8-2,5 0.20 0.50 0.80 0,6-0,9 11,0-13,0 0.3 0.20 - - - 0.15 0.10 0.02 2.1
GOST 1583-93 АК12 ММгН basis 0,8-1,5 0,85-1,35 0.20 0.20 0.60 11,0-13,0 0,8-1,3 0.20 0.20 - - 0.05 0.01 0.02 1.0
GOST 1583-93 АК9 basis 1.0 0,25-0,45 0,2-0,5 0.50 0.80 8,0-11,0 0.3 - - - - - - 0.02 2.4
GOST 1583-93 АК9пч basis 0.10 0,25-0,35 0,2-0,35 0.30 0.30 9,0-10,5 B 0,10 0,08-0,15 - 0.15 0.10 0.03 0.01 0.02 0.60
GOST 1583-93 АК8М3 basis 2,0-4,5 0.45 0.50 1.2 1.3 7,5-10,0 0.5 - - - - Pb+Sn 0,30 - 0.02 4.1
GOST 1583-93 АК7пч basis 0.10 0,25-0,45 0.10 0.20 0.40 7,0-8,0 B 0,10 0.08 - 0.15 0.10 0.03 0.01 0.02 0.70
GOST 4784-97 АД31 basis 0.10 0,45-0,9 0.10 0.20 0.50 0,2-0,6 - 0.15 0.10 - - - - 0.05 0.15